Ingizo la joto la kulehemu ni nini na kwa nini ni muhimu?

Heat input Q = (η × V × I × 60) / (S × 1000) in kJ/mm, where η is thermal efficiency, V is voltage, I is current, and S is travel speed. It controls weld bead size, HAZ width, distortion, residual stress, and mechanical properties. Too high = grain coarsening; too low = lack of fusion.

Viwango vya ufanisi wa joto kwa michakato tofauti ya kulehemu ni vipi?

Per EN 1011-1: SAW = 1.0, SMAW = 0.8, MIG/MAG = 0.8, FCAW = 0.8, TIG = 0.6. These account for heat lost to radiation and convection rather than entering the workpiece.

Muda wa kupoa t8/5 ni nini?

t8/5 is the time (seconds) for the weld HAZ to cool from 800°C to 500°C. This controls the microstructure: short t8/5 → martensite (hard, brittle); long t8/5 → ferrite/pearlite (softer, tougher). Target: 5-25 seconds for most carbon steels.

Joto la awali linaainishwaje?

Joto la awali linategemea sawa la kaboni (CE), unene wa bamba, ingizo la joto, na maudhui ya hidrojeni. Kwa CE 0.45: 150-250°C. Kulingana na AWS D1.1 Jedwali 3.3 pamoja na marekebisho ya unene.

ISO 4063 classifies welding processes by reference numbers: 111=SMAW, 131=MIG, 135=MAG, 136=FCAW, 141=TIG, 121=SAW. Used on drawings, WPS documents, and welder qualifications.

Zana ya Uhandisi Isiyolipisha

Kikokotoo cha Ingizo la Joto la Kulehemu & ISO 4063

Hesabu ingizo la joto (kJ/mm), muda wa kupozwa t8/5, mapendekezo ya joto la awali, na sawa la kaboni. Inajumuisha kumbukumbu ya mchakato wa ISO 4063.

ISO 4063 EN 1011-1 Ingizo la Joto kJ/mm

Mchakato wa Kulehemu

Arc Voltage (V)

Mkondo wa Kulehemu (A)

Travel Speed (mm/min)

Unene wa Bamba (mm)

Sawa la Kaboni CE (IIW formula)

Quick presets

Results

Heat Input Q

—

Ufanisi wa Joto η

—

Nishati ya Arc (bila η)

—

Muda wa Kupozwa t8/5 (makadirio)

—

Sawa la Kaboni CE

—

Mapendekezo ya Kupasha Joto Kabla ya Kulehemu

—

Tathmini ya Uwezo wa Kulehemu

—

Mchakato wa ISO 4063

—

Hesabu ya Ingizo la Joto (EN 1011-1)

Ingizo la joto ni nishati inayotolewa kwa kila kitengo cha urefu wa kulehemu:

η — sababu ya ufanisi wa joto (inategemea mchakato)
V — voltaji ya arc (volts)
I — mkondo wa kulehemu (amps)
S — kasi ya usafiri (mm/min)

Vipengele vya Ufanisi wa Joto

ISO 4063 No.	Process	η (EN 1011-1)
121	SAW (arc iliyozikwa)	1.0
111	SMAW (fimbo / MMA)	0.8
131	MIG (gesi isiyoshiriki)	0.8
135	MAG (active gas)	0.8
136	FCAW (msingi wa flux)	0.8
141	TIG / GTAW	0.6

Ukadiriaji wa Muda wa Kupoa t8/5

The time to cool from 800°C to 500°C determines the resulting microstructure. Simplified Rosenthal 2D model for thick plates:

Sawa la Kaboni & Joto la Awali

Fomula ya sawa la kaboni ya IIW inatabiri uwezo wa kulehemu na mahitaji ya joto la awali:

Mfano wa Vitendo

Mfano — Kulehemu kwa MAG bamba la S355 la 20 mm

Given: Process 135 (η=0.8), V=28V, I=250A, S=300 mm/min, CE=0.42

Arc energy = (28 × 250 × 60) / (300 × 1000) = 1.40 kJ/mm

Heat input Q = 0.8 × 1.40 = 1.12 kJ/mm

CE = 0.42 → Uwezo wa kulehemu wa wastani, joto la awali linahitajika 100–150°C recommended

⚠️ Note: Ukadiriaji wa t8/5 ni rahisi. Kupoa halisi kunategemea jiometri ya kiungo, joto la awali, joto kati ya safu, na hali ya mazingira. Rejelea EN 1011-2 kwa matumizi muhimu.

No.	Process	Maelezo	η
111	SMAW	Arc ya chuma iliyolindwa (fimbo/MMA)	0.8
114	FCAW-S	Msingi wa flux unaojilinda mwenyewe	0.8
121	SAW	Kulehemu kwa arc iliyozikwa	1.0
131	MIG	Gesi isiyoshiriki ya chuma (Ar) — alumini, SS	0.8
135	MAG	Metal active gas (CO₂/Ar+CO₂) — carbon steel	0.8
136	FCAW-G	Flux-cored + active gas	0.8
137	FCAW-G	Waya wa msingi wa flux + gesi ajizi	0.8
138	MCAW	Metal-cored wire + active gas	0.8
141	TIG	Gesi ajizi ya tungsten (GTAW)	0.6
15	Plasma	Kulehemu kwa arc ya plasma	0.6
311	OAW	Kulehemu kwa oxy-acetilini	0.45
42	Friction	Kulehemu kwa msuguano	—
52	Laser	Kulehemu kwa mwangaza wa leza	0.9

Kikokotoo cha Ingizo la Joto la Kulehemu & Marejeo ya ISO 4063

Published by Nikolai Shelkovenko on Febuari 15, 2026 Machi 5, 2026

Results

Hesabu ya Ingizo la Joto (EN 1011-1)

Vipengele vya Ufanisi wa Joto

Ukadiriaji wa Muda wa Kupoa t8/5

Sawa la Kaboni & Joto la Awali

Mfano wa Vitendo

Duka

Support

Contact