Šta je toplinski unos pri zavarivanju i zašto je važan?

Heat input Q = (η × V × I × 60) / (S × 1000) in kJ/mm, where η is thermal efficiency, V is voltage, I is current, and S is travel speed. It controls weld bead size, HAZ width, distortion, residual stress, and mechanical properties. Too high = grain coarsening; too low = lack of fusion.

Koja su toplotna efikasnost faktori za različite procese zavarivanja?

Per EN 1011-1: SAW = 1.0, SMAW = 0.8, MIG/MAG = 0.8, FCAW = 0.8, TIG = 0.6. These account for heat lost to radiation and convection rather than entering the workpiece.

Šta je vrijeme hlađenja t8/5?

t8/5 is the time (seconds) for the weld HAZ to cool from 800°C to 500°C. This controls the microstructure: short t8/5 → martensite (hard, brittle); long t8/5 → ferrite/pearlite (softer, tougher). Target: 5-25 seconds for most carbon steels.

Kako se određuje temperatura predgrijavanja?

Predgrijavanje zavisi od ekvivalenta ugljika (CE), debljine ploče, toplinskog unosa i sadržaja vodonika. Za CE 0.45: 150-250°C. Per AWS D1.1 Table 3.3 with adjustments for thickness.

ISO 4063 classifies welding processes by reference numbers: 111=SMAW, 131=MIG, 135=MAG, 136=FCAW, 141=TIG, 121=SAW. Used on drawings, WPS documents, and welder qualifications.

Besplatan Inženjerski Alat

Kalkulator toplinskog unosa pri zavarivanju i ISO 4063

Izračunajte toplinski unos (kJ/mm), vrijeme hlađenja t8/5, preporuku zagrijavanja i ekvivalent ugljenika. Uključuje referensu ISO 4063 procesa.

ISO 4063 EN 1011-1 Toplinski unos kJ/mm

Proces zavarivanja

Arc Voltage (V)

Struja zavarivanja (A)

Travel Speed (mm/min)

Debljina ploče (mm)

Ekvivalent ugljenika CE (IIW formula)

Quick presets

Results

Heat Input Q

—

Toplotna efikasnost η

—

Energija luka (bez η)

—

Vrijeme hlađenja t8/5 (procjena)

—

Ekvivalent ugljenika CE

—

Preporuka za predgrijavanje

—

Procjena zavarljivosti

—

ISO 4063 Process

—

Proračun unosa topline (EN 1011-1)

Unos topline je energija dovedena po jedinici dužine zavara:

η — faktor toplotne efikasnosti (zavisan od procesa)
V — napon luka (volti)
I — struja zavarivanja (amperi)
S — brzina kretanja (mm/min)

Faktori toplotne efikasnosti

ISO 4063 No.	Process	η (EN 1011-1)
121	SAW (zavareni potopljeni luk)	1.0
111	SMAW (štapni / MMA)	0.8
131	MIG (inertni gas)	0.8
135	MAG (active gas)	0.8
136	FCAW (flux-core)	0.8
141	TIG / GTAW	0.6

Procjena vremena hlađenja t8/5

The time to cool from 800°C to 500°C determines the resulting microstructure. Simplified Rosenthal 2D model for thick plates:

Ekvivalent ugljika & Predgrijavanje

IIW formula ekvivalenta ugljika predviđa zavarljivost i potrebe za predgrijavanjem:

Praktični primjer

Primer — MAG zavarivanje ploče S355 debljine 20 mm

Given: Process 135 (η=0.8), V=28V, I=250A, S=300 mm/min, CE=0.42

Arc energy = (28 × 250 × 60) / (300 × 1000) = 1.40 kJ/mm

Heat input Q = 0.8 × 1.40 = 1.12 kJ/mm

CE = 0.42 → Dobra zavarljivost, predgrijavanje 100–150°C recommended

⚠️ Note: Procjena t8/5 je pojednostavljena. Stvarno hlađenje ovisi o geometriji spoja, pregrijavanju, međutemperaturi i vanjskim uvjetima. Za kritične primjene konzultirajte EN 1011-2.

No.	Process	Opis	η
111	SMAW	Zaštićeni metal-lučni (štapni/MMA)	0.8
114	FCAW-S	Samoštitna fluks-jezgra	0.8
121	SAW	Potopljeno lučno zavarivanje	1.0
131	MIG	Metal u inertnom plinu (Ar) — aluminij, nehrđajući čelik	0.8
135	MAG	Metal active gas (CO₂/Ar+CO₂) — carbon steel	0.8
136	FCAW-G	Flux-cored + active gas	0.8
137	FCAW-G	Fluks-jezgra + inertni plin	0.8
138	MCAW	Metal-cored wire + active gas	0.8
141	TIG	Volfram u inertnom plinu (GTAW)	0.6
15	Plasma	Plazmno lučno zavarivanje	0.6
311	OAW	Oksi-acetilensko zavarivanje	0.45
42	Friction	Zavarivanje trenjem	—
52	Laser	Zavarivanje laserskom zrakom	0.9

Kalkulator toplinskog unosa pri zavarivanju i referenca ISO 4063

Published by Nikolai Shelkovenko on Februar 15, 2026 Mart 5, 2026

Results

Proračun unosa topline (EN 1011-1)

Faktori toplotne efikasnosti

Procjena vremena hlađenja t8/5

Ekvivalent ugljika & Predgrijavanje

Praktični primjer