Kietumo keitiklis
Konvertuoti tarp Rokvelo HRC, Brinelio HB, Vikerso HV ir Rokvelo HRB kietumo skalių. Remiantis ASTM E140 konversijos duomenimis su tiesine interpoliacija.
Rezultatai
HRC diapazonas (grūdinti plienai)
| HRC | Aukštavertė | HB | Rm (MPa) |
|---|---|---|---|
| 20 | 238 | 228 | ~787 |
| 25 | 255 | 243 | ~838 |
| 30 | 279 | 266 | ~918 |
| 35 | 331 | 311 | ~1073 |
| 40 | 392 | 360 | ~1242 |
| 45 | 458 | 421 | ~1452 |
| 50 | 542 | 484 | ~1670 |
| 55 | 595 | 544 | ~1877 |
| 60 | 697 | — | — |
| 65 | 832 | — | — |
HRB diapazonas (minkštesni plienai)
| HRB | Aukštavertė | HB | Rm (MPa) |
|---|---|---|---|
| 60 | 107 | 105 | ~362 |
| 70 | 120 | 118 | ~407 |
| 80 | 141 | 138 | ~476 |
| 90 | 171 | 166 | ~573 |
| 100 | 210 | 202 | ~697 |
ℹ️ Pastaba: Vertės tarp lentelės įrašų apskaičiuojamos naudojant tiesinę interpoliaciją. HB vertės, didesnės nei HRC 55, paprastai nematuojamos (medžiaga per kieta rutuliniam įspaudikliui). Tempiamojo stiprumo įverčiai taikomi tik angliniam ir legiruotam plienui.
Rokvelo kietumas (HRC / HRB)
Rokvelo testas matuoja įsiskverbimo gylis esant didelei apkrovai, palyginti su išankstiniu įtempimu. Tai greita, paprasta ir plačiai naudojama gamyboje.
- HRC — Deimantinis kūginis (Brale) įspaudiklis, 150 kgf pagrindinė apkrova. Diapazonas: 20–70 HRC. Grūdintam plienui.
- HRB — 1/16 colio plieninis rutulys, 100 kgf pagrindinė apkrova. Diapazonas: 20–100 HRB. Minkštesniam plienui, žalvariui, aliuminiui.
Vikerso kietumas (HV)
Naudoja deimantinį piramidinį įspaudiklį su kintama apkrova (1–120 kgf). Matuoja įdubos įstrižainė. Tinka visiems kietumo diapazonams – nuo labai minkšto iki labai kieto.
Brinelio kietumas (HB)
Naudoja 10 mm volframo karbido rutulį su 3000 kgf apkrova (plienui). Matuoja įdubos skersmuo. Geriausiai tinka stambiagrūdėms medžiagoms, tokioms kaip liejiniai.
Tempimo stiprumo apytikslis įvertinimas
⚠️ Svarbu: Rm ≈ 3,45 × HB santykis yra apytikslis ir galioja tik angliniams ir legiruotiems plienams, kurių kietumas yra ~100–400 HB. Nenaudokite nerūdijančiam plienui, ketui, spalvotiesiems metalams arba grūdintam plienui, kurio kietumas didesnis nei ~55 HRC.
Praktinis pavyzdys
Atsižvelgiant į tai, kad: Išmatuotas kietumas = 45 HRC
Iš ASTM E140 lentelės: HRC 45 ≈ HV 458 ≈ HB 421
Apskaičiuotas tempiamasis stipris: Rm ≈ 3,45 × 421 = ~1452 MPa
Each scale uses a different indenter and load:
- HRC (Rockwell C) — Diamond cone, 150 kgf. For hardened steels (20–70 HRC).
- HRB (Rockwell B) — 1/16" steel ball, 100 kgf. For softer materials (20–100 HRB).
- HV (Vickers) — Diamond pyramid, variable load. Universal range, very precise.
- HB (Brinell) — 10 mm carbide ball, 3000 kgf. For castings, larger test areas.
General guidance:
- HRC — Hardened and tempered steels, tool steels, case-hardened parts
- HRB — Annealed steels, brass, aluminum, softer metals
- HV — Thin sheets, coatings, micro-hardness, wide range of materials
- HB — Castings, forgings, raw stock, weld HAZ testing
When in doubt, use HRC for hardened steels and HV for everything else.
Different hardness tests measure different physical properties:
- Rockwell measures depth of penetration
- Vickers measures area of indentation
- Brinell measures diameter of indentation
Since these are fundamentally different measurements, the relationships between them are empirical (based on testing), not mathematical. Results vary by material type, microstructure, and heat treatment condition.
ASTM E140 provides accepted approximate conversions based on extensive testing of carbon and alloy steels.
For carbon and alloy steels, the approximate relationship is:
- Rm (MPa) ≈ 3.45 × HB
- Rm (psi) ≈ 500 × HB
This is valid for the range of approximately 100–400 HB. Above ~55 HRC, this relationship breaks down as materials become brittle.
Do not use this for stainless steels, cast irons, non-ferrous metals, or materials with unusual microstructures.
Rockwell (ASTM E18): Apply preload (10 kgf), then major load (60/100/150 kgf). Measure depth increase. Quick (~10s), portable, minimal surface preparation.
Vickers (ASTM E92/E384): Force a diamond pyramid into the surface. Measure both diagonals under microscope. Very precise, works for micro-hardness (HV 0.01) to macro (HV 120).
Brinell (ASTM E10): Press a 10 mm ball into the surface with 3000 kgf (for steel). Measure indentation diameter. Averages over a large area — ideal for heterogeneous materials like castings.
Šiame puslapyje aprašytas procedūras sukūrė ir lauko sąlygomis išbandė Vibromera komanda, naudodama Balanset-1A – nešiojamą dviejų kanalų balansavimo įrenginį ir vibracijų analizatorių rotoriams balansuoti vietoje.
Profesionalūs lauko balansavimo prietaisai ir programinė įranga. Naudojami daugiau nei 50 šalių.
Nikolai Shelkovenko
Nikolai Shelkovenko yra vibracijos analizės inžinierius bei „Vibromera“ įkūrėjas ir generalinis direktorius. Daugiau nei 15 metų jis balansavo besisukančią įrangą lauko sąlygomis, o ne bandymų stende: mulčiuotuvus, pramoninius ventiliatorius, smulkintuvus, centrifugas, velenus ir špindelius. Būtent iš šio darbo išaugo „Balanset“ prietaisai — jie buvo sukurti kaip įrankis, kurį specialistas gali atsinešti prie mašinos ir naudoti savarankiškai, vietoje, o ne kaip laboratorinę įrangą. „Vibromera“ įkurta 2017 metais, nuo 2023 metų įsikūrusi Porto mieste, Portugalijoje. Čia vyksta visas „Balanset“ linijos kūrimas, surinkimas ir palaikymas. Pagrindinis prietaisas — „Balanset-1A“, nešiojamas analizatorius vienos ir dviejų plokštumų balansavimui bei vibracijos diagnostikai. Nikolai asmeniškai dalyvauja klientų aptarnavime, sudėtingų balansavimo atvejų sprendime ir programinės įrangos kūrime. Jis dirba su klientais visame pasaulyje, bet kuria kalba.