Pretvarač tvrdoće
Pretvara tvrdoću između skala tvrdoće Rockwell HRC, Brinell HB, Vickers HV i Rockwell HRB. Na temelju podataka o pretvorbi ASTM E140 s linearnom interpolacijom.
Rezultati
HRC raspon (kaljeni čelici)
| HRC | HV | HB | Rm (MPa) |
|---|---|---|---|
| 20 | 238 | 228 | ~787 |
| 25 | 255 | 243 | ~838 |
| 30 | 279 | 266 | ~918 |
| 35 | 331 | 311 | ~1073 |
| 40 | 392 | 360 | ~1242 |
| 45 | 458 | 421 | ~1452 |
| 50 | 542 | 484 | ~1670 |
| 55 | 595 | 544 | ~1877 |
| 60 | 697 | — | — |
| 65 | 832 | — | — |
HRB raspon (mekši čelici)
| HRB | HV | HB | Rm (MPa) |
|---|---|---|---|
| 60 | 107 | 105 | ~362 |
| 70 | 120 | 118 | ~407 |
| 80 | 141 | 138 | ~476 |
| 90 | 171 | 166 | ~573 |
| 100 | 210 | 202 | ~697 |
ℹ️ Napomena: Vrijednosti između unosa u tablici izračunavaju se linearnom interpolacijom. Vrijednosti HB iznad HRC 55 obično se ne mjere (materijal je pretvrd za kuglični utiskivač). Procjene vlačne čvrstoće primjenjuju se samo na ugljične i legirane čelike.
Tvrdoća po Rockwellu (HRC / HRB)
Rockwellov test mjeri dubina prodiranja pod velikim opterećenjem u usporedbi s predopterećenjem. Brz je, jednostavan i široko se koristi u proizvodnji.
- HRC — Dijamantni konusni (Brale) utiskivač, glavno opterećenje 150 kgf. Raspon tvrdoće: 20–70 HRC. Za kaljene čelike.
- HRB — Čelična kugla 1/16″, glavno opterećenje 100 kgf. Raspon: 20–100 HRB. Za mekše čelike, mesing, aluminij.
Tvrdoća po Vickersu (HV)
Koristi dijamantni piramidalni utiskivač s promjenjivim opterećenjem (1–120 kgf). Mjeri dijagonala udubljenja. Radi za sve raspone tvrdoće, od vrlo mekog do vrlo tvrdog.
Tvrdoća po Brinellu (HB)
Koristi kuglicu od volframovog karbida promjera 10 mm s opterećenjem od 3000 kgf (za čelik). Mjeri promjer udubljenja. Najbolje za grubozrnate materijale poput odljevaka.
Približna vrijednost vlačne čvrstoće
⚠️ Važno: Odnos Rm ≈ 3,45 × HB je približan i vrijedi samo za ugljične i legirane čelike u rasponu od ~100 do 400 HB. Ne koristiti za nehrđajuće čelike, lijevano željezo, obojene metale ili kaljene čelike iznad ~55 HRC.
Praktični primjer
Dano: Izmjerena tvrdoća = 45 HRC
Iz tablice ASTM E140: HRC 45 ≈ HV 458 ≈ HB 421
Procijenjena vlačna čvrstoća: Rm ≈ 3,45 × 421 = ~1452 MPa
Each scale uses a different indenter and load:
- HRC (Rockwell C) — Diamond cone, 150 kgf. For hardened steels (20–70 HRC).
- HRB (Rockwell B) — 1/16" steel ball, 100 kgf. For softer materials (20–100 HRB).
- HV (Vickers) — Diamond pyramid, variable load. Universal range, very precise.
- HB (Brinell) — 10 mm carbide ball, 3000 kgf. For castings, larger test areas.
General guidance:
- HRC — Hardened and tempered steels, tool steels, case-hardened parts
- HRB — Annealed steels, brass, aluminum, softer metals
- HV — Thin sheets, coatings, micro-hardness, wide range of materials
- HB — Castings, forgings, raw stock, weld HAZ testing
When in doubt, use HRC for hardened steels and HV for everything else.
Different hardness tests measure different physical properties:
- Rockwell measures depth of penetration
- Vickers measures area of indentation
- Brinell measures diameter of indentation
Since these are fundamentally different measurements, the relationships between them are empirical (based on testing), not mathematical. Results vary by material type, microstructure, and heat treatment condition.
ASTM E140 provides accepted approximate conversions based on extensive testing of carbon and alloy steels.
For carbon and alloy steels, the approximate relationship is:
- Rm (MPa) ≈ 3.45 × HB
- Rm (psi) ≈ 500 × HB
This is valid for the range of approximately 100–400 HB. Above ~55 HRC, this relationship breaks down as materials become brittle.
Do not use this for stainless steels, cast irons, non-ferrous metals, or materials with unusual microstructures.
Rockwell (ASTM E18): Apply preload (10 kgf), then major load (60/100/150 kgf). Measure depth increase. Quick (~10s), portable, minimal surface preparation.
Vickers (ASTM E92/E384): Force a diamond pyramid into the surface. Measure both diagonals under microscope. Very precise, works for micro-hardness (HV 0.01) to macro (HV 120).
Brinell (ASTM E10): Press a 10 mm ball into the surface with 3000 kgf (for steel). Measure indentation diameter. Averages over a large area — ideal for heterogeneous materials like castings.
Postupke opisane na ovoj stranici razvio je i terenski testirao tim Vibromera koristeći Balanset-1A, prijenosni dvokanalni balanser i analizator vibracija za balansiranje rotora na terenu.
Profesionalni instrumenti i softver za balansiranje na terenu. Koriste se u više od 50 zemalja.
Nikolai Shelkovenko
Nikolai Shelkovenko inženjer je analize vibracija te osnivač i izvršni direktor tvrtke Vibromera. Više od 15 godina balansira rotacijsku opremu na terenu, a ne na ispitnom stolu: malčere, industrijske ventilatore, drobilice, centrifuge, vratila i vretena. Upravo je iz tog rada nastala oprema Balanset — osmišljena je kao alat koji stručnjak može ponijeti do stroja i sam njime raditi na licu mjesta, a ne kao laboratorijska oprema. Vibromera je osnovana 2017. godine, a od 2023. sjedište joj je u Portu u Portugalu. Ovdje se odvijaju razvoj, sklapanje i podrška za liniju Balanset. Vodeći instrument je Balanset-1A, prijenosni analizator za balansiranje u jednoj i dvije ravnine te za dijagnostiku vibracija. Nikolai je osobno uključen u podršku korisnicima, u rješavanje složenih slučajeva balansiranja i u razvoj programske podrške. Radi s korisnicima diljem svijeta, na bilo kojem jeziku.