Převodník tvrdosti
Převod mezi stupnicemi tvrdosti Rockwell HRC, Brinell HB, Vickers HV a Rockwell HRB. Na základě konverzních dat ASTM E140 s lineární interpolací.
Výsledky
Rozsah HRC (kalené oceli)
| HRC | HV | HB | Rm (MPa) |
|---|---|---|---|
| 20 | 238 | 228 | ~787 |
| 25 | 255 | 243 | ~838 |
| 30 | 279 | 266 | ~918 |
| 35 | 331 | 311 | ~1073 |
| 40 | 392 | 360 | ~1242 |
| 45 | 458 | 421 | ~1452 |
| 50 | 542 | 484 | ~1670 |
| 55 | 595 | 544 | ~1877 |
| 60 | 697 | - | - |
| 65 | 832 | - | - |
Rozsah HRB (měkčí oceli)
| HRB | HV | HB | Rm (MPa) |
|---|---|---|---|
| 60 | 107 | 105 | ~362 |
| 70 | 120 | 118 | ~407 |
| 80 | 141 | 138 | ~476 |
| 90 | 171 | 166 | ~573 |
| 100 | 210 | 202 | ~697 |
ℹ️ Poznámka: Hodnoty mezi položkami tabulky se vypočítávají pomocí lineární interpolace. Hodnoty HB nad HRC 55 se obvykle neměří (materiál je pro kuličkovou vtlačovací sondu příliš tvrdý). Odhady pevnosti v tahu platí pouze pro uhlíkové a legované oceli.
Tvrdost podle Rockwella (HRC / HRB)
Rockwellův test měří hloubka vniknutí při velkém zatížení ve srovnání s předpětím. Je to rychlé, snadné a široce používané ve výrobě.
- HRC — Diamantový kuželový (Braleův) penetrátor, hlavní zatížení 150 kgf. Rozsah tvrdosti: 20–70 HRC. Pro kalené oceli.
- HRB — Ocelová kulička 1/16″, hlavní zatížení 100 kgf. Rozsah: 20–100 HRB. Pro měkčí oceli, mosaz, hliník.
Tvrdost podle Vickerse (HV)
Používá diamantový pyramidový penetrátor s proměnným zatížením (1–120 kgf). Měří diagonála vtisku. Funguje pro všechny stupně tvrdosti, od velmi měkkých po velmi tvrdé.
Tvrdost podle Brinella (HB)
Používá kuličku z karbidu wolframu o průměru 10 mm se zatížením 3000 kgf (pro ocel). Měří průměr vtisku. Nejlepší pro hrubozrnné materiály, jako jsou odlitky.
Aproximace pevnosti v tahu
⚠️ Důležité: Vztah Rm ≈ 3,45 × HB je přibližný a platí pouze pro uhlíkové a legované oceli v rozsahu ~100–400 HB. Nepoužívejte pro nerezové oceli, litiny, neželezné kovy nebo kalené oceli s tvrdostí nad ~55 HRC.
Praktický příklad
Vzhledem k: Naměřená tvrdost = 45 HRC
Z tabulky ASTM E140: HRC 45 ≈ HV 458 ≈ HB 421
Odhadovaná pevnost v tahu: Rm ≈ 3,45 × 421 = ~1452 MPa
Each scale uses a different indenter and load:
- HRC (Rockwell C) — Diamond cone, 150 kgf. For hardened steels (20–70 HRC).
- HRB (Rockwell B) — 1/16" steel ball, 100 kgf. For softer materials (20–100 HRB).
- HV (Vickers) — Diamond pyramid, variable load. Universal range, very precise.
- HB (Brinell) — 10 mm carbide ball, 3000 kgf. For castings, larger test areas.
General guidance:
- HRC — Hardened and tempered steels, tool steels, case-hardened parts
- HRB — Annealed steels, brass, aluminum, softer metals
- HV — Thin sheets, coatings, micro-hardness, wide range of materials
- HB — Castings, forgings, raw stock, weld HAZ testing
When in doubt, use HRC for hardened steels and HV for everything else.
Different hardness tests measure different physical properties:
- Rockwell measures depth of penetration
- Vickers measures area of indentation
- Brinell measures diameter of indentation
Since these are fundamentally different measurements, the relationships between them are empirical (based on testing), not mathematical. Results vary by material type, microstructure, and heat treatment condition.
ASTM E140 provides accepted approximate conversions based on extensive testing of carbon and alloy steels.
For carbon and alloy steels, the approximate relationship is:
- Rm (MPa) ≈ 3.45 × HB
- Rm (psi) ≈ 500 × HB
This is valid for the range of approximately 100–400 HB. Above ~55 HRC, this relationship breaks down as materials become brittle.
Do not use this for stainless steels, cast irons, non-ferrous metals, or materials with unusual microstructures.
Rockwell (ASTM E18): Apply preload (10 kgf), then major load (60/100/150 kgf). Measure depth increase. Quick (~10s), portable, minimal surface preparation.
Vickers (ASTM E92/E384): Force a diamond pyramid into the surface. Measure both diagonals under microscope. Very precise, works for micro-hardness (HV 0.01) to macro (HV 120).
Brinell (ASTM E10): Press a 10 mm ball into the surface with 3000 kgf (for steel). Measure indentation diameter. Averages over a large area — ideal for heterogeneous materials like castings.
Postupy popsané na této stránce vyvinul a v terénu otestoval tým Vibromera pomocí přístroje Balanset-1A, přenosného dvoukanálového vyvažovacího přístroje a analyzátoru vibrací pro vyvažování rotorů na místě.
Profesionální přístroje a software pro vyvažování v terénu. Používají se ve více než 50 zemích.
Nikolai Shelkovenko
Nikolai Shelkovenko je inženýr vibrační analýzy a zakladatel a generální ředitel společnosti Vibromera. Více než 15 let vyvažuje rotační stroje přímo v provozu, a ne na zkušebním stavu: mulčovače, průmyslové ventilátory, drtiče, odstředivky, hřídele a vřetena. Právě z této práce vzešly přístroje Balanset — byly navrženy jako nástroj, který si odborník může vzít ke stroji a použít sám, přímo na místě, nikoli jako laboratorní vybavení. Vibromera byla založena v roce 2017 a od roku 2023 sídlí v portugalském Portu. Zde probíhá vývoj, montáž i podpora řady Balanset. Vlajkovým přístrojem je Balanset-1A, přenosný analyzátor pro vyvažování v jedné a ve dvou rovinách a pro diagnostiku vibrací. Nikolai se osobně podílí na zákaznické podpoře, na řešení obtížných případů vyvažování i na vývoji softwaru. Pracuje se zákazníky po celém světě, v jakémkoli jazyce.