Bezplatný inžiniersky nástroj
Prevodník tvrdosti
Prevod medzi stupnicami tvrdosti Rockwell HRC, Brinell HB, Vickers HV a Rockwell HRB. Na základe konverzných údajov ASTM E140 s lineárnou interpoláciou.
Výsledky
Rozsah HRC (kalené ocele)
| HRC | HV | HB | Rm (MPa) |
|---|---|---|---|
| 20 | 238 | 228 | ~787 |
| 25 | 255 | 243 | ~838 |
| 30 | 279 | 266 | ~918 |
| 35 | 331 | 311 | ~1073 |
| 40 | 392 | 360 | ~1242 |
| 45 | 458 | 421 | ~1452 |
| 50 | 542 | 484 | ~1670 |
| 55 | 595 | 544 | ~1877 |
| 60 | 697 | — | — |
| 65 | 832 | — | — |
Rad HRB (mäkšie ocele)
| HRB | HV | HB | Rm (MPa) |
|---|---|---|---|
| 60 | 107 | 105 | ~362 |
| 70 | 120 | 118 | ~407 |
| 80 | 141 | 138 | ~476 |
| 90 | 171 | 166 | ~573 |
| 100 | 210 | 202 | ~697 |
ℹ️ Poznámka: Hodnoty medzi položkami tabuľky sa vypočítavajú pomocou lineárnej interpolácie. Hodnoty HB nad HRC 55 sa zvyčajne nemerajú (materiál je príliš tvrdý pre guľôčkové vnikacie teliesko). Odhady pevnosti v ťahu platia len pre uhlíkové a legované ocele.
Tvrdosť podľa Rockwella (HRC / HRB)
Rockwellov test meria hĺbka penetrácie pri veľkom zaťažení v porovnaní s predpätím. Je to rýchle, jednoduché a široko používané vo výrobe.
- HRC — Diamantový kužeľový (Brale) vnikacie teliesko, hlavné zaťaženie 150 kgf. Rozsah tvrdosti: 20 – 70 HRC. Pre kalené ocele.
- HRB — Oceľová guľôčka 1/16″, hlavné zaťaženie 100 kgf. Rozsah: 20–100 HRB. Pre mäkšie ocele, mosadz, hliník.
Tvrdosť podľa Vickersa (HV)
Používa diamantové pyramídové vtlačovacie teliesko s premenlivým zaťažením (1 – 120 kgf). Meria uhlopriečka vtlačku. Funguje pre všetky stupne tvrdosti, od veľmi mäkkej po veľmi tvrdú.
Tvrdosť podľa Brinella (HB)
Používa 10 mm guľôčku z karbidu volfrámu so zaťažením 3000 kgf (pre oceľ). Meria priemer vtlačku. Najlepšie pre hrubozrnné materiály, ako sú odliatky.
Aproximácia pevnosti v ťahu
⚠️ Dôležité: Vzťah Rm ≈ 3,45 × HB je približný a platí len pre uhlíkové a legované ocele v rozsahu ~100 – 400 HB. Nepoužívajte pre nehrdzavejúce ocele, liatiny, neželezné kovy alebo kalené ocele s tvrdosťou nad ~55 HRC.
Praktický príklad
Vzhľadom na to, že: Nameraná tvrdosť = 45 HRC
Z tabuľky ASTM E140: HRC 45 ≈ HV 458 ≈ HB 421
Odhadovaná pevnosť v ťahu: Rm ≈ 3,45 × 421 = ~1452 MPa
Each scale uses a different indenter and load:
- HRC (Rockwell C) — Diamond cone, 150 kgf. For hardened steels (20–70 HRC).
- HRB (Rockwell B) — 1/16" steel ball, 100 kgf. For softer materials (20–100 HRB).
- HV (Vickers) — Diamond pyramid, variable load. Universal range, very precise.
- HB (Brinell) — 10 mm carbide ball, 3000 kgf. For castings, larger test areas.
General guidance:
- HRC — Hardened and tempered steels, tool steels, case-hardened parts
- HRB — Annealed steels, brass, aluminum, softer metals
- HV — Thin sheets, coatings, micro-hardness, wide range of materials
- HB — Castings, forgings, raw stock, weld HAZ testing
When in doubt, use HRC for hardened steels and HV for everything else.
Different hardness tests measure different physical properties:
- Rockwell measures depth of penetration
- Vickers measures area of indentation
- Brinell measures diameter of indentation
Since these are fundamentally different measurements, the relationships between them are empirical (based on testing), not mathematical. Results vary by material type, microstructure, and heat treatment condition.
ASTM E140 provides accepted approximate conversions based on extensive testing of carbon and alloy steels.
For carbon and alloy steels, the approximate relationship is:
- Rm (MPa) ≈ 3.45 × HB
- Rm (psi) ≈ 500 × HB
This is valid for the range of approximately 100–400 HB. Above ~55 HRC, this relationship breaks down as materials become brittle.
Do not use this for stainless steels, cast irons, non-ferrous metals, or materials with unusual microstructures.
Rockwell (ASTM E18): Apply preload (10 kgf), then major load (60/100/150 kgf). Measure depth increase. Quick (~10s), portable, minimal surface preparation.
Vickers (ASTM E92/E384): Force a diamond pyramid into the surface. Measure both diagonals under microscope. Very precise, works for micro-hardness (HV 0.01) to macro (HV 120).
Brinell (ASTM E10): Press a 10 mm ball into the surface with 3000 kgf (for steel). Measure indentation diameter. Averages over a large area — ideal for heterogeneous materials like castings.
Postupy opísané na tejto stránke vyvinul a v teréne otestoval tím Vibromera pomocou zariadenia Balanset-1A, prenosného dvojkanálového vyvažovacieho prístroja a analyzátora vibrácií na vyvažovanie rotorov priamo na mieste.
Profesionálne prístroje a softvér na vyvažovanie v teréne. Používajú sa vo viac ako 50 krajinách.
Nikolai Shelkovenko
Nikolai Shelkovenko je inžinier vibračnej analýzy a zakladateľ a generálny riaditeľ spoločnosti Vibromera. Viac než 15 rokov vyvažuje rotačné stroje priamo v prevádzke, a nie na skúšobnom stave: mulčovače, priemyselné ventilátory, drviče, odstredivky, hriadele a vretená. Práve z tejto práce vznikli prístroje Balanset — boli navrhnuté ako nástroj, ktorý si odborník môže vziať k stroju a použiť sám, priamo na mieste, nie ako laboratórne vybavenie. Vibromera bola založená v roku 2017 a od roku 2023 sídli v portugalskom Porte. Tu prebieha vývoj, montáž aj podpora radu Balanset. Vlajkovým prístrojom je Balanset-1A, prenosný analyzátor na vyvažovanie v jednej a v dvoch rovinách a na vibračnú diagnostiku. Nikolai sa osobne podieľa na zákazníckej podpore, na riešení náročných prípadov vyvažovania aj na vývoji softvéru. Pracuje so zákazníkmi po celom svete, v akomkoľvek jazyku.