Konvertoni midis shkallëve të fortësisë Rockwell HRC, Brinell HB, Vickers HV dhe Rockwell HRB. Bazuar në të dhënat e konvertimit ASTM E140 me interpolim linear.
Rezultatet
Diapazoni HRC (Çeliqe të Fortësuara)
| HRC | HV | HB | Rm (MPa) |
|---|---|---|---|
| 20 | 238 | 228 | ~787 |
| 25 | 255 | 243 | ~838 |
| 30 | 279 | 266 | ~918 |
| 35 | 331 | 311 | ~1073 |
| 40 | 392 | 360 | ~1242 |
| 45 | 458 | 421 | ~1452 |
| 50 | 542 | 484 | ~1670 |
| 55 | 595 | 544 | ~1877 |
| 60 | 697 | — | — |
| 65 | 832 | — | — |
Diapazoni HRB (Çeliqe më të Buta)
| HRB | HV | HB | Rm (MPa) |
|---|---|---|---|
| 60 | 107 | 105 | ~362 |
| 70 | 120 | 118 | ~407 |
| 80 | 141 | 138 | ~476 |
| 90 | 171 | 166 | ~573 |
| 100 | 210 | 202 | ~697 |
ℹ️ Shënim: Vlerat midis hyrjeve të tabelës llogariten duke përdorur interpolim linear. Vlerat HB mbi HRC 55 zakonisht nuk maten (materiali shumë i fortë për penetruesin me top). Vlerësimet e rezistencës në tërheqje vlejnë vetëm për çeliqet me karbon dhe çeliqet e lidhura.
Fortësia Rockwell (HRC / HRB)
Testi Rockwell mat thellësinë e depërtimit nën një ngarkesë të madhe krahasuar me një para-ngarkesë. Është i shpejtë, i lehtë dhe përdoret gjerësisht në prodhim.
- HRC — Penetrues konik diamanti (Brale), ngarkesë kryesore 150 kgf. Diapazoni: 20–70 HRC. Për çeliqet e fortësuara.
- HRB — Top çeliku 1/16″, ngarkesë kryesore 100 kgf. Diapazoni: 20–100 HRB. Për çeliqe më të buta, tunxh, alumin.
Fortësia Vickers (HV)
Përdor një penetrues piramidal diamanti me ngarkesë të ndryshueshme (1–120 kgf). Mat diagonalen e gjurmës. Funksionon për të gjitha diapazonet e fortësisë, nga shumë i butë deri te shumë i fortë.
Fortësia Brinell (HB)
Përdor një top karbur tungsteni 10 mm me ngarkesë 3000 kgf (për çelik). Mat diametrin e gjurmës. Më i miri për materiale me kokrra të trasha, si derdhjet.
Vlerësimi i Rezistencës në Tërheqje
⚠️ E rëndësishme: Marrëdhënia Rm ≈ 3.45 × HB është e përafërt dhe vlen vetëm për çeliqet me karbon dhe çeliqet e lidhura në diapazonin ~100–400 HB. Mos e përdorni për çeliqet inox, gize, metalet jo-ferroze, ose çeliqet e fortësuara mbi ~55 HRC.
Shembull praktik
Të dhëna: Fortësia e matur = 45 HRC
Nga tabela ASTM E140: HRC 45 ≈ HV 458 ≈ HB 421
Rezistenca e vlerësuar në tërheqje: Rm ≈ 3.45 × 421 = ~1452 MPa
Each scale uses a different indenter and load:
- HRC (Rockwell C) — Diamond cone, 150 kgf. For hardened steels (20–70 HRC).
- HRB (Rockwell B) — 1/16" steel ball, 100 kgf. For softer materials (20–100 HRB).
- HV (Vickers) — Diamond pyramid, variable load. Universal range, very precise.
- HB (Brinell) — 10 mm carbide ball, 3000 kgf. For castings, larger test areas.
General guidance:
- HRC — Hardened and tempered steels, tool steels, case-hardened parts
- HRB — Annealed steels, brass, aluminum, softer metals
- HV — Thin sheets, coatings, micro-hardness, wide range of materials
- HB — Castings, forgings, raw stock, weld HAZ testing
When in doubt, use HRC for hardened steels and HV for everything else.
Different hardness tests measure different physical properties:
- Rockwell measures depth of penetration
- Vickers measures area of indentation
- Brinell measures diameter of indentation
Since these are fundamentally different measurements, the relationships between them are empirical (based on testing), not mathematical. Results vary by material type, microstructure, and heat treatment condition.
ASTM E140 provides accepted approximate conversions based on extensive testing of carbon and alloy steels.
For carbon and alloy steels, the approximate relationship is:
- Rm (MPa) ≈ 3.45 × HB
- Rm (psi) ≈ 500 × HB
This is valid for the range of approximately 100–400 HB. Above ~55 HRC, this relationship breaks down as materials become brittle.
Do not use this for stainless steels, cast irons, non-ferrous metals, or materials with unusual microstructures.
Rockwell (ASTM E18): Apply preload (10 kgf), then major load (60/100/150 kgf). Measure depth increase. Quick (~10s), portable, minimal surface preparation.
Vickers (ASTM E92/E384): Force a diamond pyramid into the surface. Measure both diagonals under microscope. Very precise, works for micro-hardness (HV 0.01) to macro (HV 120).
Brinell (ASTM E10): Press a 10 mm ball into the surface with 3000 kgf (for steel). Measure indentation diameter. Averages over a large area — ideal for heterogeneous materials like castings.
Procedurat e përshkruara në këtë faqe u zhvilluan dhe u testuan në terren nga ekipi i Vibromera duke përdorur Balanset-1A, një balancues portativ me dy kanale dhe analizues vibrimesh për balancimin e rotorëve në vend.
Instrumente dhe softuer profesional për balancim në terren. Të përdorura në mbi 50 vende.
Nikolai Shelkovenko
Nikolai Shelkovenko është inxhinier i analizës së vibrimeve, si dhe themelues dhe drejtor ekzekutiv i Vibromera. Prej më shumë se 15 vjetësh ai balancon pajisje rrotulluese në terren dhe jo në një stend prove: mulçerë, ventilatorë industrialë, thyerës, centrifuga, boshte dhe boshte punuese. Pikërisht nga kjo punë lindën instrumentet Balanset — ato u projektuan si një mjet që specialisti mund ta marrë me vete te makina dhe ta përdorë vetë, në vend, e jo si pajisje laboratori. Vibromera u themelua në vitin 2017 dhe që nga viti 2023 e ka selinë në Porto, Portugali. Këtu zhvillohen projektimi, montimi dhe mbështetja e linjës Balanset. Instrumenti kryesor është Balanset-1A, një analizues portativ për balancim në një dhe në dy rrafshe dhe për diagnostikimin e vibrimeve. Nikolai merr pjesë personalisht në mbështetjen e klientëve, në zgjidhjen e rasteve të vështira të balancimit dhe në zhvillimin e programit. Ai punon me klientë në mbarë botën, në çdo gjuhë.