Gratis ingeniørværktøj
Hårdhedskonverter
Konverter mellem Rockwell HRC, Brinell HB, Vickers HV og Rockwell HRB hårdhedsskalaer. Baseret på ASTM E140 konverteringsdata med lineær interpolation.
Resultater
HRC-serie (hærdede stål)
| HRC | HV | HB | Rm (MPa) |
|---|---|---|---|
| 20 | 238 | 228 | ~787 |
| 25 | 255 | 243 | ~838 |
| 30 | 279 | 266 | ~918 |
| 35 | 331 | 311 | ~1073 |
| 40 | 392 | 360 | ~1242 |
| 45 | 458 | 421 | ~1452 |
| 50 | 542 | 484 | ~1670 |
| 55 | 595 | 544 | ~1877 |
| 60 | 697 | — | — |
| 65 | 832 | — | — |
HRB-serien (blødere stål)
| HRB | HV | HB | Rm (MPa) |
|---|---|---|---|
| 60 | 107 | 105 | ~362 |
| 70 | 120 | 118 | ~407 |
| 80 | 141 | 138 | ~476 |
| 90 | 171 | 166 | ~573 |
| 100 | 210 | 202 | ~697 |
Bemærk: Værdier mellem tabelposter beregnes ved hjælp af lineær interpolation. HB-værdier over HRC 55 måles typisk ikke (materialet er for hårdt til kugleindtrykning). Trækstyrkeestimater gælder kun for kulstof- og legeringsstål.
Rockwell-hårdhed (HRC / HRB)
Rockwell-testen måler dybde af penetration under en stor belastning sammenlignet med en forbelastning. Det er hurtigt, nemt og bruges i vid udstrækning i produktionen.
- HRC — Diamantkegleformet (Brale) indtrykningslegeme, 150 kgf hovedbelastning. Område: 20–70 HRC. Til hærdede ståltyper.
- HRB — 1/16″ stålkugle, 100 kgf hovedbelastning. Område: 20–100 HRB. Til blødere stål, messing, aluminium.
Vickers-hårdhed (HV)
Bruger en diamantpyramideindrykningsmaskine med variabel belastning (1-120 kgf). Måler diagonalen af indrykningen. Fungerer til alle hårdhedsgrader, fra meget blød til meget hård.
Brinell-hårdhed (HB)
Bruger en 10 mm wolframkarbidkugle med en belastning på 3000 kgf (til stål). Måler diameteren af fordybningen. Bedst til grovkornede materialer som støbegods.
Tilnærmelse af trækstyrke
⚠️ Vigtigt: Forholdet Rm ≈ 3,45 × HB er omtrentligt og kun gyldigt for kulstof- og legeringsstål i området ~100-400 HB. Må ikke anvendes til rustfrit stål, støbejern, ikke-jernholdige metaller eller hærdede stål over ~55 HRC.
Praktisk eksempel
Givet: Målt hårdhed = 45 HRC
Fra ASTM E140-tabel: HRC 45 ≈ HV 458 ≈ HB 421
Estimeret trækstyrke: Rm ≈ 3,45 × 421 = ~1452 MPa
Each scale uses a different indenter and load:
- HRC (Rockwell C) — Diamond cone, 150 kgf. For hardened steels (20–70 HRC).
- HRB (Rockwell B) — 1/16" steel ball, 100 kgf. For softer materials (20–100 HRB).
- HV (Vickers) — Diamond pyramid, variable load. Universal range, very precise.
- HB (Brinell) — 10 mm carbide ball, 3000 kgf. For castings, larger test areas.
General guidance:
- HRC — Hardened and tempered steels, tool steels, case-hardened parts
- HRB — Annealed steels, brass, aluminum, softer metals
- HV — Thin sheets, coatings, micro-hardness, wide range of materials
- HB — Castings, forgings, raw stock, weld HAZ testing
When in doubt, use HRC for hardened steels and HV for everything else.
Different hardness tests measure different physical properties:
- Rockwell measures depth of penetration
- Vickers measures area of indentation
- Brinell measures diameter of indentation
Since these are fundamentally different measurements, the relationships between them are empirical (based on testing), not mathematical. Results vary by material type, microstructure, and heat treatment condition.
ASTM E140 provides accepted approximate conversions based on extensive testing of carbon and alloy steels.
For carbon and alloy steels, the approximate relationship is:
- Rm (MPa) ≈ 3.45 × HB
- Rm (psi) ≈ 500 × HB
This is valid for the range of approximately 100–400 HB. Above ~55 HRC, this relationship breaks down as materials become brittle.
Do not use this for stainless steels, cast irons, non-ferrous metals, or materials with unusual microstructures.
Rockwell (ASTM E18): Apply preload (10 kgf), then major load (60/100/150 kgf). Measure depth increase. Quick (~10s), portable, minimal surface preparation.
Vickers (ASTM E92/E384): Force a diamond pyramid into the surface. Measure both diagonals under microscope. Very precise, works for micro-hardness (HV 0.01) to macro (HV 120).
Brinell (ASTM E10): Press a 10 mm ball into the surface with 3000 kgf (for steel). Measure indentation diameter. Averages over a large area — ideal for heterogeneous materials like castings.
Procedurerne beskrevet på denne side blev udviklet og felttestet af Vibromera-teamet ved hjælp af Balanset-1A, en bærbar tokanals afbalanceringsenhed og vibrationsanalysator til afbalancering af rotorer på stedet.
Professionelle feltbalanceringsinstrumenter og software. Anvendes i over 50 lande.
Nikolai Shelkovenko
Nikolai Shelkovenko er vibrationsanalyseingeniør samt stifter og direktør for Vibromera. I mere end 15 år har han afbalanceret roterende udstyr i marken frem for på en prøvebænk: flismaskiner, industriventilatorer, knusere, centrifuger, aksler og spindler. Det er dette arbejde, Balanset-instrumenterne er vokset ud af — de blev udviklet som et værktøj, en specialist kan tage med hen til maskinen og bruge alene på stedet, ikke som laboratorieudstyr. Vibromera blev grundlagt i 2017 og har siden 2023 haft base i Porto i Portugal. Udvikling, montage og support af Balanset-serien foregår her. Flagskibet er Balanset-1A, en bærbar analysator til afbalancering i ét og to planer og til vibrationsdiagnostik. Nikolai deltager personligt i kundesupporten, i arbejdet med vanskelige afbalanceringsopgaver og i udviklingen af softwaren. Han arbejder med kunder over hele verden, på ethvert sprog.