Muunna Rockwell HRC-, Brinell HB-, Vickers HV- ja Rockwell HRB -kovuusasteikkojen välillä. Perustuu ASTM E140 -muunnostietoihin lineaarisella interpoloinnilla.
Tulokset
HRC-alue (karkaistut teräkset)
| HRC | HV | HB | Rm (MPa) |
|---|---|---|---|
| 20 | 238 | 228 | ~787 |
| 25 | 255 | 243 | ~838 |
| 30 | 279 | 266 | ~918 |
| 35 | 331 | 311 | ~1073 |
| 40 | 392 | 360 | ~1242 |
| 45 | 458 | 421 | ~1452 |
| 50 | 542 | 484 | ~1670 |
| 55 | 595 | 544 | ~1877 |
| 60 | 697 | — | — |
| 65 | 832 | — | — |
HRB-alue (pehmeämmät teräkset)
| HRB | HV | HB | Rm (MPa) |
|---|---|---|---|
| 60 | 107 | 105 | ~362 |
| 70 | 120 | 118 | ~407 |
| 80 | 141 | 138 | ~476 |
| 90 | 171 | 166 | ~573 |
| 100 | 210 | 202 | ~697 |
ℹ️ Huomautus: Taulukon merkintöjen väliset arvot lasketaan lineaarisella interpoloinnilla. HB-arvoja, jotka ovat yli HRC 55, ei tyypillisesti mitata (materiaali liian kova kuulapääkoneelle). Vetolujuusarviot koskevat vain hiili- ja seosteräksiä.
Rockwell-kovuus (HRC / HRB)
Rockwellin testi mittaa tunkeutumissyvyyden suuren kuormituksen alaisena verrattuna esikuormitukseen. Se on nopea, helppo ja laajalti käytetty tuotannossa.
- HRC — Timanttikartioinen (Brale) sisennyskärki, pääkuorma 150 kgf. Alue: 20–70 HRC. Karkaistuille teräksille.
- HRB — 1/16″ teräskuula, pääkuorma 100 kgf. Alue: 20–100 HRB. Pehmeämmille teräksille, messingille ja alumiinille.
Vickersin kovuus (HV)
Käyttää timanttipyramidi-indenteriä, jonka kuormitus on vaihteleva (1–120 kgf). Mittaa sisennyksen lävistäjän. Toimii kaikilla kovuusalueilla erittäin pehmeästä erittäin kovaan.
Brinell-kovuus (HB)
Käyttää 10 mm:n volframikarbidikuulaa ja 3000 kgf:n kuormitusta (teräkselle). Mittaa syvennyksen halkaisijan. Paras karkeille materiaaleille, kuten valukappaleille.
Vetolujuuden likimääräinen laskenta
⚠️ Tärkeää: Rm ≈ 3,45 × HB -suhde on likimääräinen ja pätee vain hiili- ja seosteräksille, joiden kovuus on välillä ~100–400 HB. Ei saa käyttää ruostumattomille teräksille, valuraudoille, ei-rautametalleille tai yli ~55 HRC:n karkaistuille teräksille.
Käytännön esimerkki
Annettu: Mitattu kovuus = 45 HRC
ASTM E140 -taulukosta: HRC 45 ≈ HV 458 ≈ HB 421
Arvioitu vetolujuus: Rm ≈ 3,45 × 421 = ~1452 MPa
Each scale uses a different indenter and load:
- HRC (Rockwell C) — Diamond cone, 150 kgf. For hardened steels (20–70 HRC).
- HRB (Rockwell B) — 1/16" steel ball, 100 kgf. For softer materials (20–100 HRB).
- HV (Vickers) — Diamond pyramid, variable load. Universal range, very precise.
- HB (Brinell) — 10 mm carbide ball, 3000 kgf. For castings, larger test areas.
General guidance:
- HRC — Hardened and tempered steels, tool steels, case-hardened parts
- HRB — Annealed steels, brass, aluminum, softer metals
- HV — Thin sheets, coatings, micro-hardness, wide range of materials
- HB — Castings, forgings, raw stock, weld HAZ testing
When in doubt, use HRC for hardened steels and HV for everything else.
Different hardness tests measure different physical properties:
- Rockwell measures depth of penetration
- Vickers measures area of indentation
- Brinell measures diameter of indentation
Since these are fundamentally different measurements, the relationships between them are empirical (based on testing), not mathematical. Results vary by material type, microstructure, and heat treatment condition.
ASTM E140 provides accepted approximate conversions based on extensive testing of carbon and alloy steels.
For carbon and alloy steels, the approximate relationship is:
- Rm (MPa) ≈ 3.45 × HB
- Rm (psi) ≈ 500 × HB
This is valid for the range of approximately 100–400 HB. Above ~55 HRC, this relationship breaks down as materials become brittle.
Do not use this for stainless steels, cast irons, non-ferrous metals, or materials with unusual microstructures.
Rockwell (ASTM E18): Apply preload (10 kgf), then major load (60/100/150 kgf). Measure depth increase. Quick (~10s), portable, minimal surface preparation.
Vickers (ASTM E92/E384): Force a diamond pyramid into the surface. Measure both diagonals under microscope. Very precise, works for micro-hardness (HV 0.01) to macro (HV 120).
Brinell (ASTM E10): Press a 10 mm ball into the surface with 3000 kgf (for steel). Measure indentation diameter. Averages over a large area — ideal for heterogeneous materials like castings.
Tällä sivulla kuvatut menetelmät on kehittänyt ja kenttätestannut Vibromera-tiimi Balanset-1A-laitteella, joka on kannettava kaksikanavainen tasapainotuslaite ja tärinäanalysaattori roottoreiden tasapainotukseen paikan päällä.
Ammattimaiset kenttätasapainotuslaitteet ja -ohjelmistot. Käytössä yli 50 maassa.
Nikolai Shelkovenko
Nikolai Shelkovenko on värähtelyanalyysi-insinööri sekä Vibromeran perustaja ja toimitusjohtaja. Yli 15 vuoden ajan hän on tasapainottanut pyöriviä koneita kentällä eikä koepenkissä: silppureita, teollisuuspuhaltimia, murskaimia, linkoja, akseleita ja karoja. Juuri tästä työstä Balanset-laitteet ovat syntyneet — ne suunniteltiin työkaluksi, jonka asiantuntija voi kantaa koneen luo ja jota hän voi käyttää yksin paikan päällä, ei laboratoriolaitteiksi. Vibromera perustettiin vuonna 2017, ja vuodesta 2023 lähtien sen kotipaikka on ollut Porto Portugalissa. Balanset-sarjan kehitys, kokoonpano ja tuki tapahtuvat täällä. Lippulaivalaite on Balanset-1A, kannettava analysaattori yhden ja kahden tason tasapainotukseen sekä värähtelydiagnostiikkaan. Nikolai osallistuu henkilökohtaisesti asiakastukeen, vaikeiden tasapainotustapausten ratkaisemiseen ja ohjelmiston kehittämiseen. Hän palvelee asiakkaita ympäri maailmaa, millä tahansa kielellä.