Hardhetskonverter
Konverter mellom hardhetsskalaene Rockwell HRC, Brinell HB, Vickers HV og Rockwell HRB. Basert på ASTM E140-konverteringsdata med lineær interpolasjon.
Resultater
HRC-serien (herdet stål)
| HRC | HV | HB | Rm (MPa) |
|---|---|---|---|
| 20 | 238 | 228 | ~787 |
| 25 | 255 | 243 | ~838 |
| 30 | 279 | 266 | ~918 |
| 35 | 331 | 311 | ~1073 |
| 40 | 392 | 360 | ~1242 |
| 45 | 458 | 421 | ~1452 |
| 50 | 542 | 484 | ~1670 |
| 55 | 595 | 544 | ~1877 |
| 60 | 697 | - | - |
| 65 | 832 | - | - |
HRB-serien (mykere stål)
| HRB | HV | HB | Rm (MPa) |
|---|---|---|---|
| 60 | 107 | 105 | ~362 |
| 70 | 120 | 118 | ~407 |
| 80 | 141 | 138 | ~476 |
| 90 | 171 | 166 | ~573 |
| 100 | 210 | 202 | ~697 |
Merknad: Verdier mellom tabelloppføringer beregnes ved hjelp av lineær interpolasjon. HB-verdier over HRC 55 måles vanligvis ikke (materialet er for hardt for kuleinnrykk). Strekkfasthetsestimater gjelder kun for karbonstål og legeringsstål.
Rockwell-hardhet (HRC / HRB)
Rockwell-testen måler penetrasjonsdybde under stor belastning sammenlignet med forbelastning. Det er raskt, enkelt og mye brukt i produksjon.
- HRC — Diamantkonus (Brale) inntrykker, 150 kgf hovedbelastning. Område: 20–70 HRC. For herdet stål.
- HRB — 1/16″ stålkule, 100 kgf hovedbelastning. Område: 20–100 HRB. For mykere stål, messing, aluminium.
Vickers-hardhet (HV)
Bruker en diamantpyramideinntrykker med variabel belastning (1–120 kgf). Måler diagonalen til innrykket. Fungerer for alle hardhetsgrader, fra veldig myk til veldig hard.
Brinell-hardhet (HB)
Bruker en 10 mm wolframkarbidkule med 3000 kgf belastning (for stål). Måler diameteren på fordypningen. Best for grovkornede materialer som støpegods.
Tilnærming av strekkfasthet
⚠️ Viktig: Forholdet Rm ≈ 3,45 × HB er omtrentlig og gjelder kun for karbonstål og legeringsstål i området ~100–400 HB. Ikke bruk for rustfritt stål, støpejern, ikke-jernholdige metaller eller herdet stål over ~55 HRC.
Praktisk eksempel
Gitt: Målt hardhet = 45 HRC
Fra ASTM E140-tabellen: HRC 45 ≈ HV 458 ≈ HB 421
Beregnet strekkfasthet: Rm ≈ 3,45 × 421 = ~1452 MPa
Each scale uses a different indenter and load:
- HRC (Rockwell C) — Diamond cone, 150 kgf. For hardened steels (20–70 HRC).
- HRB (Rockwell B) — 1/16" steel ball, 100 kgf. For softer materials (20–100 HRB).
- HV (Vickers) — Diamond pyramid, variable load. Universal range, very precise.
- HB (Brinell) — 10 mm carbide ball, 3000 kgf. For castings, larger test areas.
General guidance:
- HRC — Hardened and tempered steels, tool steels, case-hardened parts
- HRB — Annealed steels, brass, aluminum, softer metals
- HV — Thin sheets, coatings, micro-hardness, wide range of materials
- HB — Castings, forgings, raw stock, weld HAZ testing
When in doubt, use HRC for hardened steels and HV for everything else.
Different hardness tests measure different physical properties:
- Rockwell measures depth of penetration
- Vickers measures area of indentation
- Brinell measures diameter of indentation
Since these are fundamentally different measurements, the relationships between them are empirical (based on testing), not mathematical. Results vary by material type, microstructure, and heat treatment condition.
ASTM E140 provides accepted approximate conversions based on extensive testing of carbon and alloy steels.
For carbon and alloy steels, the approximate relationship is:
- Rm (MPa) ≈ 3.45 × HB
- Rm (psi) ≈ 500 × HB
This is valid for the range of approximately 100–400 HB. Above ~55 HRC, this relationship breaks down as materials become brittle.
Do not use this for stainless steels, cast irons, non-ferrous metals, or materials with unusual microstructures.
Rockwell (ASTM E18): Apply preload (10 kgf), then major load (60/100/150 kgf). Measure depth increase. Quick (~10s), portable, minimal surface preparation.
Vickers (ASTM E92/E384): Force a diamond pyramid into the surface. Measure both diagonals under microscope. Very precise, works for micro-hardness (HV 0.01) to macro (HV 120).
Brinell (ASTM E10): Press a 10 mm ball into the surface with 3000 kgf (for steel). Measure indentation diameter. Averages over a large area — ideal for heterogeneous materials like castings.
Prosedyrene som er beskrevet på denne siden, ble utviklet og testet i felt av Vibromera-teamet med Balanset-1A, en bærbar tokanals balanserer og vibrasjonsanalysator for balansering av rotorer på stedet.
Profesjonelle feltbalanseringsinstrumenter og programvare. Brukes i over 50 land.
Nikolai Shelkovenko
Nikolai Shelkovenko er vibrasjonsanalyseingeniør samt grunnlegger og daglig leder i Vibromera. I mer enn 15 år har han balansert roterende utstyr ute i felt i stedet for på en prøvebenk: mulchmaskiner, industrivifter, knusere, sentrifuger, aksler og spindler. Det er ut av dette arbeidet Balanset-instrumentene har vokst — de ble utformet som et verktøy en fagperson kan ta med til maskinen og bruke alene på stedet, ikke som laboratorieutstyr. Vibromera ble grunnlagt i 2017 og har siden 2023 hatt base i Porto i Portugal. Utvikling, montering og støtte for Balanset-serien skjer her. Flaggskipet er Balanset-1A, en bærbar analysator for balansering i ett og to plan og for vibrasjonsdiagnostikk. Nikolai deltar personlig i kundestøtten, i arbeidet med vanskelige balanseringssaker og i utviklingen av programvaren. Han jobber med kunder over hele verden, på alle språk.