Brezplačno inženirsko orodje
Pretvornik trdote
Pretvarjanje med lestvicami trdote Rockwell HRC, Brinell HB, Vickers HV in Rockwell HRB. Na podlagi podatkov o pretvorbi ASTM E140 z linearno interpolacijo.
Rezultati
HRC območje (kaljena jekla)
| HRC | HV | HB | Rm (MPa) |
|---|---|---|---|
| 20 | 238 | 228 | ~787 |
| 25 | 255 | 243 | ~838 |
| 30 | 279 | 266 | ~918 |
| 35 | 331 | 311 | ~1073 |
| 40 | 392 | 360 | ~1242 |
| 45 | 458 | 421 | ~1452 |
| 50 | 542 | 484 | ~1670 |
| 55 | 595 | 544 | ~1877 |
| 60 | 697 | — | — |
| 65 | 832 | — | — |
HRB serija (mehkejša jekla)
| HRB | HV | HB | Rm (MPa) |
|---|---|---|---|
| 60 | 107 | 105 | ~362 |
| 70 | 120 | 118 | ~407 |
| 80 | 141 | 138 | ~476 |
| 90 | 171 | 166 | ~573 |
| 100 | 210 | 202 | ~697 |
ℹ️ Opomba: Vrednosti med vnosi v tabeli so izračunane z linearno interpolacijo. Vrednosti HB nad HRC 55 se običajno ne merijo (material je pretrd za vtiskovalnik s kroglico). Ocene natezne trdnosti veljajo samo za ogljikova in legirana jekla.
Trdota po Rockwellu (HRC / HRB)
Rockwellov test meri globina penetracije pod veliko obremenitvijo v primerjavi s prednapetostjo. Je hiter, enostaven in se pogosto uporablja v proizvodnji.
- HRC — Vtiskovalnik z diamantnim stožcem (Brale), glavna obremenitev 150 kgf. Območje trdote: 20–70 HRC. Za kaljena jekla.
- HRB — Jeklena krogla 1/16″, glavna obremenitev 100 kgf. Območje: 20–100 HRB. Za mehkejša jekla, medenino, aluminij.
Trdota po Vickersu (HV)
Uporablja diamantno piramidalno vtiskovalno orodje s spremenljivo obremenitvijo (1–120 kgf). Meri diagonala vdolbine. Deluje za vse trdote, od zelo mehke do zelo trde.
Trdota po Brinellu (HB)
Uporablja 10 mm volframovo karbidno kroglico z obremenitvijo 3000 kgf (za jeklo). Meri premer vdolbine. Najboljše za grobozrnate materiale, kot so ulitki.
Približek natezne trdnosti
⚠️ Pomembno: Razmerje Rm ≈ 3,45 × HB je približno in velja le za ogljikova in legirana jekla v območju ~100–400 HB. Ne uporabljajte za nerjavna jekla, lito železo, barvne kovine ali kaljena jekla nad ~55 HRC.
Praktični primer
Dano: Izmerjena trdota = 45 HRC
Iz tabele ASTM E140: HRC 45 ≈ HV 458 ≈ HB 421
Ocenjena natezna trdnost: Rm ≈ 3,45 × 421 = ~1452 MPa
Each scale uses a different indenter and load:
- HRC (Rockwell C) — Diamond cone, 150 kgf. For hardened steels (20–70 HRC).
- HRB (Rockwell B) — 1/16" steel ball, 100 kgf. For softer materials (20–100 HRB).
- HV (Vickers) — Diamond pyramid, variable load. Universal range, very precise.
- HB (Brinell) — 10 mm carbide ball, 3000 kgf. For castings, larger test areas.
General guidance:
- HRC — Hardened and tempered steels, tool steels, case-hardened parts
- HRB — Annealed steels, brass, aluminum, softer metals
- HV — Thin sheets, coatings, micro-hardness, wide range of materials
- HB — Castings, forgings, raw stock, weld HAZ testing
When in doubt, use HRC for hardened steels and HV for everything else.
Different hardness tests measure different physical properties:
- Rockwell measures depth of penetration
- Vickers measures area of indentation
- Brinell measures diameter of indentation
Since these are fundamentally different measurements, the relationships between them are empirical (based on testing), not mathematical. Results vary by material type, microstructure, and heat treatment condition.
ASTM E140 provides accepted approximate conversions based on extensive testing of carbon and alloy steels.
For carbon and alloy steels, the approximate relationship is:
- Rm (MPa) ≈ 3.45 × HB
- Rm (psi) ≈ 500 × HB
This is valid for the range of approximately 100–400 HB. Above ~55 HRC, this relationship breaks down as materials become brittle.
Do not use this for stainless steels, cast irons, non-ferrous metals, or materials with unusual microstructures.
Rockwell (ASTM E18): Apply preload (10 kgf), then major load (60/100/150 kgf). Measure depth increase. Quick (~10s), portable, minimal surface preparation.
Vickers (ASTM E92/E384): Force a diamond pyramid into the surface. Measure both diagonals under microscope. Very precise, works for micro-hardness (HV 0.01) to macro (HV 120).
Brinell (ASTM E10): Press a 10 mm ball into the surface with 3000 kgf (for steel). Measure indentation diameter. Averages over a large area — ideal for heterogeneous materials like castings.
Postopki, opisani na tej strani, so bili razviti in terensko preizkušeni s strani ekipe Vibromera z uporabo naprave Balanset-1A, prenosnega dvokanalnega uravnoteževalnika in analizatorja vibracij za uravnoteženje rotorjev na mestu uporabe.
Profesionalni instrumenti in programska oprema za uravnoteženje na terenu. Uporabljajo se v več kot 50 državah.
Nikolai Shelkovenko
Nikolai Shelkovenko je inženir vibracijske analize ter ustanovitelj in izvršni direktor podjetja Vibromera. Že več kot 15 let uravnotežuje vrtečo se opremo na terenu, in ne na preizkuševališču: mulčerje, industrijske ventilatorje, drobilnike, centrifuge, gredi in vretena. Prav iz tega dela so nastali instrumenti Balanset — zasnovani so bili kot orodje, ki ga strokovnjak lahko prinese do stroja in ga uporabi sam, na mestu samem, ne pa kot laboratorijska oprema. Vibromera je bila ustanovljena leta 2017, od leta 2023 pa ima sedež v Portu na Portugalskem. Tu potekajo razvoj, sestavljanje in podpora za linijo Balanset. Vodilni instrument je Balanset-1A, prenosni analizator za enoravninsko in dvoravninsko uravnoteženje ter za vibracijsko diagnostiko. Nikolai osebno sodeluje pri podpori strankam, pri reševanju zahtevnih primerov uravnoteženja in pri razvoju programske opreme. S strankami dela po vsem svetu, v katerem koli jeziku.