Cietības pārveidotājs
Konvertēt starp Rokvela HRC, Brinela HB, Vikersa HV un Rokvela HRB cietības skalām. Balstoties uz ASTM E140 konvertēšanas datiem ar lineāru interpolāciju.
Rezultāti
HRC diapazons (rūdīti tēraudi)
| HRC | HV | HB | Rm (MPa) |
|---|---|---|---|
| 20 | 238 | 228 | ~787 |
| 25 | 255 | 243 | ~838 |
| 30 | 279 | 266 | ~918 |
| 35 | 331 | 311 | ~1073 |
| 40 | 392 | 360 | ~1242 |
| 45 | 458 | 421 | ~1452 |
| 50 | 542 | 484 | ~1670 |
| 55 | 595 | 544 | ~1877 |
| 60 | 697 | — | — |
| 65 | 832 | — | — |
HRB diapazons (mīkstāki tēraudi)
| HRB | HV | HB | Rm (MPa) |
|---|---|---|---|
| 60 | 107 | 105 | ~362 |
| 70 | 120 | 118 | ~407 |
| 80 | 141 | 138 | ~476 |
| 90 | 171 | 166 | ~573 |
| 100 | 210 | 202 | ~697 |
Piezīme: Vērtības starp tabulas ierakstiem tiek aprēķinātas, izmantojot lineāru interpolāciju. HB vērtības virs HRC 55 parasti netiek mērītas (materiāls ir pārāk ciets lodīšu iespiešanas urbim). Stiepes izturības aprēķini attiecas tikai uz oglekļa un leģētajiem tēraudiem.
Rokvela cietība (HRC / HRB)
Rokvela tests mēra iespiešanās dziļums zem lielas slodzes, salīdzinot ar iepriekšēju slodzi. Tas ir ātri, vienkārši un plaši izmantots ražošanā.
- HRC — Dimanta konusa (Brale) iespīlētājs, 150 kgf galvenā slodze. Diapazons: 20–70 HRC. Rūdītiem tēraudiem.
- HRB — 1/16 collas tērauda lodīte, 100 kgf galvenā slodze. Diapazons: 20–100 HRB. Mīkstākam tēraudam, misiņam, alumīnijam.
Vikersa cietība (HV)
Izmanto dimanta piramīdas iespiešanas instrumentu ar mainīgu slodzi (1–120 kgf). Mēra ievilkuma diagonāle. Der visām cietības pakāpēm – no ļoti mīkstas līdz ļoti cietai.
Brinela cietība (HB)
Izmanto 10 mm volframa karbīda lodīti ar 3000 kgf slodzi (tēraudam). Mēra iedobuma diametrs. Vislabāk piemērots rupji graudainiem materiāliem, piemēram, lējumiem.
Stiepes izturības aproksimācija
⚠️ Svarīgi: Rm ≈ 3,45 × HB attiecība ir aptuvena un derīga tikai oglekļa un leģētajiem tēraudiem diapazonā no ~100 līdz 400 HB. Nelietot nerūsējošajiem tēraudiem, čuguniem, krāsainajiem metāliem vai rūdītiem tēraudiem, kuru cietība pārsniedz ~55 HRC.
Praktisks piemērs
Ņemot vērā: Izmērītā cietība = 45 HRC
No ASTM E140 tabulas: HRC 45 ≈ HV 458 ≈ HB 421
Paredzamā stiepes izturība: Rm ≈ 3,45 × 421 = ~ 1452 MPa
Each scale uses a different indenter and load:
- HRC (Rockwell C) — Diamond cone, 150 kgf. For hardened steels (20–70 HRC).
- HRB (Rockwell B) — 1/16" steel ball, 100 kgf. For softer materials (20–100 HRB).
- HV (Vickers) — Diamond pyramid, variable load. Universal range, very precise.
- HB (Brinell) — 10 mm carbide ball, 3000 kgf. For castings, larger test areas.
General guidance:
- HRC — Hardened and tempered steels, tool steels, case-hardened parts
- HRB — Annealed steels, brass, aluminum, softer metals
- HV — Thin sheets, coatings, micro-hardness, wide range of materials
- HB — Castings, forgings, raw stock, weld HAZ testing
When in doubt, use HRC for hardened steels and HV for everything else.
Different hardness tests measure different physical properties:
- Rockwell measures depth of penetration
- Vickers measures area of indentation
- Brinell measures diameter of indentation
Since these are fundamentally different measurements, the relationships between them are empirical (based on testing), not mathematical. Results vary by material type, microstructure, and heat treatment condition.
ASTM E140 provides accepted approximate conversions based on extensive testing of carbon and alloy steels.
For carbon and alloy steels, the approximate relationship is:
- Rm (MPa) ≈ 3.45 × HB
- Rm (psi) ≈ 500 × HB
This is valid for the range of approximately 100–400 HB. Above ~55 HRC, this relationship breaks down as materials become brittle.
Do not use this for stainless steels, cast irons, non-ferrous metals, or materials with unusual microstructures.
Rockwell (ASTM E18): Apply preload (10 kgf), then major load (60/100/150 kgf). Measure depth increase. Quick (~10s), portable, minimal surface preparation.
Vickers (ASTM E92/E384): Force a diamond pyramid into the surface. Measure both diagonals under microscope. Very precise, works for micro-hardness (HV 0.01) to macro (HV 120).
Brinell (ASTM E10): Press a 10 mm ball into the surface with 3000 kgf (for steel). Measure indentation diameter. Averages over a large area — ideal for heterogeneous materials like castings.
Šajā lapā aprakstītās procedūras izstrādāja un lauka apstākļos pārbaudīja Vibromera komanda, izmantojot Balanset-1A — pārnēsājamu divkanālu balansētāju un vibrāciju analizatoru rotoru balansēšanai uz vietas.
Profesionāli lauka balansēšanas instrumenti un programmatūra. Izmanto vairāk nekā 50 valstīs.
Nikolai Shelkovenko
Nikolai Shelkovenko ir vibrāciju analīzes inženieris, kā arī uzņēmuma Vibromera dibinātājs un vadītājs. Vairāk nekā 15 gadus viņš balansē rotējošas iekārtas darba vietā, nevis uz pārbaudes stenda: mulčētājus, rūpnieciskos ventilatorus, drupinātājus, centrifūgas, vārpstas un darbvārpstas. Tieši no šī darba radās Balanset instrumenti — tie tika veidoti kā rīks, ko speciālists var aiznest pie mašīnas un lietot viens pats uz vietas, nevis kā laboratorijas aprīkojums. Vibromera dibināta 2017. gadā, un kopš 2023. gada tā atrodas Portu, Portugālē. Šeit notiek Balanset līnijas izstrāde, montāža un atbalsts. Vadošais instruments ir Balanset-1A — portatīvs analizators balansēšanai vienā un divās plaknēs, kā arī vibrāciju diagnostikai. Nikolai personīgi piedalās klientu atbalstā, sarežģītu balansēšanas gadījumu risināšanā un programmatūras izstrādē. Viņš strādā ar klientiem visā pasaulē, jebkurā valodā.