Konverter Tvrdoće
Pretvarajte između Rockwell HRC, Brinell HB, Vickers HV i Rockwell HRB skala tvrdoće. Zasnovano na ASTM E140 konverzijskim podacima sa linearnom interpolacijom.
Rezultati
HRC Raspon (Hartovani Čelik)
| HRC | HV | HB | Rm (MPa) |
|---|---|---|---|
| 20 | 238 | 228 | ~787 |
| 25 | 255 | 243 | ~838 |
| 30 | 279 | 266 | ~918 |
| 35 | 331 | 311 | ~1073 |
| 40 | 392 | 360 | ~1242 |
| 45 | 458 | 421 | ~1452 |
| 50 | 542 | 484 | ~1670 |
| 55 | 595 | 544 | ~1877 |
| 60 | 697 | — | — |
| 65 | 832 | — | — |
HRB Raspon (Mekši Čelik)
| HRB | HV | HB | Rm (MPa) |
|---|---|---|---|
| 60 | 107 | 105 | ~362 |
| 70 | 120 | 118 | ~407 |
| 80 | 141 | 138 | ~476 |
| 90 | 171 | 166 | ~573 |
| 100 | 210 | 202 | ~697 |
ℹ️ Napomena: Vrijednosti između unosa u tablici se izračunavaju linearnom interpolacijom. HB vrijednosti iznad HRC 55 se obično ne mjere (materijal je previše tvrd za kuglasto usitnjivač). Procjene vlačne čvrstoće primjenjuju se samo na ugljični i legirani čelik.
Rockwellova Tvrdoća (HRC / HRB)
Rockwellov test mjeri dubinu penetracije pod velikim opterećenjem u odnosu na predopterećenje. Brz je, jednostavan i široko korišten u proizvodnji.
- HRC — Dijamantni konus (Brale) usitnjivač, 150 kgf glavno opterećenje. Raspon: 20–70 HRC. Za hartovani čelik.
- HRB — 1/16″ čelična kuglica, 100 kgf glavno opterećenje. Raspon: 20–100 HRB. Za mekši čelik, messing, aluminij.
Vickerova Tvrdoća (HV)
Koristi dijamantni piramidni usitnjivač sa promjenjivim opterećenjem (1–120 kgf). Mjeri dijagonalu otiska. Radi za sve raspone tvrdoće od vrlo mekog do vrlo tvrdog.
Brinellova Tvrdoća (HB)
Koristi 10 mm kuglicu od volframa sa 3000 kgf opterećenja (za čelik). Mjeri promjer otiska. Najbolje za sitnozrnate materijale poput livenja.
Aproksimacija Vlačne Čvrstoće
⚠️ Važno: Odnos Rm ≈ 3.45 × HB je približan i vrijedi samo za ugljične i legirane čelike u rasponu ~100–400 HB. Ne koristiti za nehrđajuće čelike, lijevano gvožđe, obojene metale ili kaljene čelike iznad ~55 HRC.
Praktični primjer
Zadano: Izmjerena tvrdoća = 45 HRC
Iz tabele ASTM E140: HRC 45 ≈ HV 458 ≈ HB 421
Procijenjena zatezna čvrstoća: Rm ≈ 3.45 × 421 = ~1452 MPa
Each scale uses a different indenter and load:
- HRC (Rockwell C) — Diamond cone, 150 kgf. For hardened steels (20–70 HRC).
- HRB (Rockwell B) — 1/16" steel ball, 100 kgf. For softer materials (20–100 HRB).
- HV (Vickers) — Diamond pyramid, variable load. Universal range, very precise.
- HB (Brinell) — 10 mm carbide ball, 3000 kgf. For castings, larger test areas.
General guidance:
- HRC — Hardened and tempered steels, tool steels, case-hardened parts
- HRB — Annealed steels, brass, aluminum, softer metals
- HV — Thin sheets, coatings, micro-hardness, wide range of materials
- HB — Castings, forgings, raw stock, weld HAZ testing
When in doubt, use HRC for hardened steels and HV for everything else.
Different hardness tests measure different physical properties:
- Rockwell measures depth of penetration
- Vickers measures area of indentation
- Brinell measures diameter of indentation
Since these are fundamentally different measurements, the relationships between them are empirical (based on testing), not mathematical. Results vary by material type, microstructure, and heat treatment condition.
ASTM E140 provides accepted approximate conversions based on extensive testing of carbon and alloy steels.
For carbon and alloy steels, the approximate relationship is:
- Rm (MPa) ≈ 3.45 × HB
- Rm (psi) ≈ 500 × HB
This is valid for the range of approximately 100–400 HB. Above ~55 HRC, this relationship breaks down as materials become brittle.
Do not use this for stainless steels, cast irons, non-ferrous metals, or materials with unusual microstructures.
Rockwell (ASTM E18): Apply preload (10 kgf), then major load (60/100/150 kgf). Measure depth increase. Quick (~10s), portable, minimal surface preparation.
Vickers (ASTM E92/E384): Force a diamond pyramid into the surface. Measure both diagonals under microscope. Very precise, works for micro-hardness (HV 0.01) to macro (HV 120).
Brinell (ASTM E10): Press a 10 mm ball into the surface with 3000 kgf (for steel). Measure indentation diameter. Averages over a large area — ideal for heterogeneous materials like castings.
Procedure opisane na ovoj stranici razvio je i terenski testirao tim Vibromera koristeći Balanset-1A, prenosivi dvokanalni balanser i analizator vibracija za balansiranje rotora na licu mjesta.
Profesionalni instrumenti i softver za balansiranje na terenu. Koristi se u 50+ zemalja.
Nikolai Shelkovenko
Nikolai Shelkovenko je inženjer analize vibracija te osnivač i izvršni direktor kompanije Vibromera. Više od 15 godina balansira rotacionu opremu na terenu, a ne na ispitnom stolu: malčere, industrijske ventilatore, drobilice, centrifuge, vratila i vretena. Upravo je iz tog rada nastala serija instrumenata Balanset — osmišljeni su kao alat koji stručnjak može ponijeti do mašine i njime raditi sam, na licu mjesta, a ne kao laboratorijska oprema. Vibromera je osnovana 2017. godine, a od 2023. sjedište joj je u Portu u Portugalu. Ovdje se odvijaju razvoj, sklapanje i podrška za liniju Balanset. Vodeći instrument je Balanset-1A, prijenosni analizator za balansiranje u jednoj i dvije ravni te za vibracijsku dijagnostiku. Nikolai lično učestvuje u podršci korisnicima, u rješavanju složenih slučajeva balansiranja i u razvoju softvera. Radi s korisnicima širom svijeta, na bilo kojem jeziku.