What is the difference between hardness scales?

HRC (Rockwell C) uses a diamond cone indenter with 150 kgf load, suitable for hardened steels (20-70 HRC). HRB (Rockwell B) uses a 1/16" steel ball with 100 kgf, for softer materials (20-100 HRB). HV (Vickers) uses a diamond pyramid with variable load, suitable for all ranges. HB (Brinell) uses a 10 mm carbide ball with 3000 kgf load, best for castings and softer steels.

When should I use which hardness scale?

Use HRC for hardened and tempered steels above ~20 HRC. Use HRB for annealed and softer steels below ~100 HRB. Use HV for thin materials, coatings, case-hardened surfaces, and when a wide range is needed. Use HB for castings, forgings, and when a large test area is acceptable.

Why are hardness conversions approximate?

Different hardness tests use different indenters, loads, and measurement methods. The relationship between scales is not purely mathematical but empirical, based on testing many material samples. ASTM E140 provides accepted conversion tables, but exact conversions depend on the specific material, its condition, and microstructure.

How do I estimate tensile strength from hardness?

For carbon and alloy steels, a common approximation is Rm (MPa) ≈ 3.45 × HB. This is a rough estimate valid for steels in the range of approximately 100-400 HB. For stainless steels, non-ferrous metals, or very hard steels, this relationship does not apply accurately.

What test methods do these scales use?

Rockwell (HRC/HRB): measures depth of indentation under a specific load. Quick and portable. Vickers (HV): measures diagonal of a diamond pyramid indentation under variable load. Very precise, works for all hardness ranges. Brinell (HB): measures diameter of a ball indentation under high load. Good for averaging over larger areas (castings, welds).

Herramienta de ingeniería gratuita

Conversor de dureza

Convierte entre las escalas de dureza Rockwell HRC, Brinell HB, Vickers HV y Rockwell HRB. Basado en datos de conversión de ASTM E140 con interpolación lineal.

ASTM E140 HRC ↔ HB ↔ HV Resistencia a la Tracción

Resultados

HRC (Rockwell C)

—

HRC (Rockwell C)

—

HB (Brinell)

—

HV (Vickers)

—

HRB (Rockwell B)

—

Resistencia a la Tracción Aprox. Rm (acero)

—

Rm ≈ 3.45 × HB (aproximado, para aceros al carbono y aleados)

Rango HRC (Aceros Endurecidos)

HRC	HV	HB	Rm (MPa)
20	238	228	~787
25	255	243	~838
30	279	266	~918
35	331	311	~1073
40	392	360	~1242
45	458	421	~1452
50	542	484	~1670
55	595	544	~1877
60	697	—	—
65	832	—	—

Rango HRB (Aceros Más Blandos)

HRB	HV	HB	Rm (MPa)
60	107	105	~362
70	120	118	~407
80	141	138	~476
90	171	166	~573
100	210	202	~697

ℹ️ Nota: Los valores entre las entradas de la tabla se calculan mediante interpolación lineal. Los valores HB por encima de HRC 55 generalmente no se miden (material demasiado duro para el indentador de bola). Las estimaciones de resistencia a la tracción aplican solo a aceros al carbono y aleados.

Dureza Rockwell (HRC / HRB)

La prueba Rockwell mide la profundidad de penetración bajo una carga mayor en comparación con una precarga. Es rápida, fácil y ampliamente utilizada en producción.

HRC — Indentador de cono de diamante (Brale), carga mayor de 150 kgf. Rango: 20–70 HRC. Para aceros endurecidos.
HRB — Bola de acero de 1/16″, carga mayor de 100 kgf. Rango: 20–100 HRB. Para aceros más blandos, latón, aluminio.

Dureza Vickers (HV)

Utiliza un indentador de pirámide de diamante con carga variable (1–120 kgf). Mide la diagonal de la indentación. Funciona para todos los rangos de dureza, desde muy blando hasta muy duro.

Dureza Brinell (HB)

Utiliza una bola de carburo de tungsteno de 10 mm con carga de 3000 kgf (para acero). Mide el diámetro de la indentación. Ideal para materiales de grano grueso como fundiciones.

Aproximación de la Resistencia a la Tracción

⚠️ Importante: La relación Rm ≈ 3.45 × HB es aproximada y solo válida para aceros al carbono y aleados en el rango ~100–400 HB. No utilizar para aceros inoxidables, hierros fundidos, metales no ferrosos o aceros endurecidos por encima de ~55 HRC.

Ejemplo práctico

Ejemplo — Acero Templado y Revenido

Datos: Dureza medida = 45 HRC

De la tabla ASTM E140: HRC 45 ≈ HV 458 ≈ HB 421

Resistencia a la tracción estimada: Rm ≈ 3.45 × 421 = ~1452 MPa